Description•HCR Compounding MM 360T來地HT is a special silicone rubber文煙 with good mechan校風ical properties designed to resist 民慢high temperature 腦玩up to 315ºC and is ver開近y easy for processing and color pigmen舊線t.

AdvantagesMM 360THT is 315°C approved in綠年 the lab,however, customers 志坐are still suggested to have a high 吃子heat resistance 明舊test based on their own requirements雨話.

Characteristics •Appearance Creamy White

•Gravity.1.15

•Tensile Strength(水下Kgf/cm)83

•Elongation at break %815

•Tear Strength(Kgf/cmD)47

•Hardness(Shore A)61

Properties

After WorkingCuring Condition:

Measures on product catalysed with 75男農% dimethyl–2, 5 bis (tertiobut都如yl-peroxy), 2,5 hex村影ane, and vulcanization fo開鄉r 3 minutes at 170 °C

1.After a hours post-cur影分e at 200°C

Shore A hardness, approx 58

Tensile strength, MPa, approx.10

Elongation at break %, app她綠rox.815

Tear strength, Kn多冷/m, approx.40

2. 250°C

3days7days10days

Shore A hardnes通呢s606265

Tensile strength, MPa9.79.18.0

Elongation at break,%700645600

3. 275°C

3days7days10days

Shore A hardness636772

Tensile strength, MPa98.47.2

Elongation at break,%710600550

2. 300°C

3days7days10days

Shore A hardness656980

Tensile strength, MPa8.17.56.5

Elongation at break,%570385235